Influence of surface passivation on optical properties of spray pyrolysis deposited Pd-F:SnO2
Date
2014Author
Mwathe, Patrick Mwinzi
Musembi, Robinson
Munji, Mathew
Odari, Benjamin
Munguti, Lawrence
Ntilakigwa, Alex Alfred
Nguu, John
Aduda, Bernard
Muthoka, Boniface
Language
enMetadata
Show full item recordAbstract
Pd-F:SnO2 thin films have been prepared by spray pyrolysis technique using an alcoholic precursor solution
consisting of stannic chloride (SnCl4.5H20), ammonium fluoride (NH4F) and palladium chloride (PdCl2). Optimization on the
deposition parameters has been done in order to obtain high quality thin films. The effect of varying the fluorine content on
the optical properties of Pd-F:SnO2 thin films were studied. Data for transmittance and reflectance in the wavelength range
from 300nm – 2500nm was measured using the solid spec 3700DUV spectrophotometer. The calculated optical band gap of
the as prepared thin films has been found to range from 3.8eV to 4.11eV. Fluorine incorporation for Pd-F:SnO2 has been
found to have a narrowing effect on the band gap, but at its higher concentration the band gap has been seen to increase. The
band gap narrowing is due to the incorporation of F- ions in the crystal lattice therefore giving rise to donor levels in the SnO2
band gap which is an essential characteristic for the gas sensor applications. Both annealing and passivation have been found
to have very insignificant change in optical band gap of Pd-F:SnO2
Citation
International Journal of Materials Science and Applications 2014; 3(5): 137-142Publisher
Science Publishing Group
Subject
Spray PyrolysisFluorine Doping
Palladium Doping
Co-Doping
Palladium and Fluorine Co-Doping
Annealing
Passivation
Pd and F Co-Doped SnO2 (Pd-F:SnO2)